Chinese translation for "quenching temperature"

淬火温度

Related Translations:

ms quenching:  分级淬火

flash quenching:  喷射淬火

quenching conditions:  淬火条件

quenching nozzle:  喷射冷却器

quenching agent:  淬火剂猝光剂猝灭剂猝熄剂

quenching cracks:  淬火裂纹

quenched combustion:  急冷燃烧

end quench:  顶端淬火末端淬火

quenching defect:  淬火缺陷淬火致缺陷

quenching pulse:  熄灭脉冲猝熄脉冲

Example Sentences:

	1.	The influences of isothermal quenching temperature on the retained austenite and mechanical properties of adi were studied 摘要研究了等温淬火温度对adi中残余奥氏体及其力学性能的影响。
	2.	Quenching and tempering were chosen to strengthen the material . the quenching temperature and time were adjusted based on the hardness measurement 选择淬火和回火作为本课题的热处理工艺，并用硬度法确定可行的淬火温度和保温时间。
	3.	The results show that , with the quenching temperature ( 270 ~ 380 ) increasing , the carbon content and percentage content of retained austenite increase first and then decrease , which are up to a maximum value at 360 ; the tensile strength of adi decreases ; the elongation and impact ductility of adi increase first and then decrease , which are up to a maximum value at 360 ; but the hardness of adi decreases first and then increases , which is up to a minimum value at 360 结果表明，在试验温度范围内( 270 ~ 380 ) ，试样中残余奥氏体的含碳量及其含量随着等温淬火温度的升高先增大后减小，均在360等温淬火时出现最大值；抗拉强度随着等温淬火温度的升高而逐渐降低；伸长率和冲击韧度随着等温淬火温度的升高先增大后减小，在360等温淬火时出现最大值；硬度则随着等温淬火温度的升高先减小后增大，当360温淬火时硬度最低。
	4.	It was pointed out that with different chemical composition and different iso - quenching temperature , the structure morphologies of the bainite transition products are different from each other , the ferrite is the indispensable constituent , and whether there is or not carbide existing is not the necessary criterion to discern the bainite 指出不同化学成分和不同等温温度时贝氏体相变产物的组织形态不同，铁素体是贝氏体中不可缺少的组成部分，以及碳化物的存在与否不是判断贝氏体的必要依据。
	5.	For the fe - 2 % c - 4 % v - 4 % mo - 5 % cr - x % w alloy system , the peak value of quenching appears in 950 - 1100 . the peak value increases with the increment of w . when the content of w is 2 % , the temperature of temper hardening is 550 . for the fe - 2 % c - 4 % v - 4 % mo - 5 % cr - 2 % w alloy , the appropriate quenching temperature can be controlled in 1000 1050 and the time of preserving heat is 12min 57 （原于百分比，人分析表明， mg的变质作用的产生是由于mg影响了合金元素的偏析，使得基体组织中合金元素含量增加，相当于使合金分配系数k更偏离于1 ，从而促进了形成缩颈、晶粒繁殖和成分过冷倾向。

Similar Words：

"quenching strain" Chinese translation, "quenching stress" Chinese translation, "quenching stresses" Chinese translation, "quenching system" Chinese translation, "quenching tank" Chinese translation, "quenching temperature range" Chinese translation, "quenching test" Chinese translation, "quenching time" Chinese translation, "quenching tower" Chinese translation, "quenching transformer" Chinese translation